LLDPE
Linear low density polyethylene (LLDPE) is a non-toxic, tasteless and odorless milky white particle with a density of 0.918~0.935g/cm3.It compared with LDPE, have high softening temperature and melt temperature, has good strength and toughness, rigidity, heat resistance, cold resistance is good wait for an advantage, but also has good environmental stress cracking resistance, resistance to impact strength, tear strength and other properties, and acid, alkali, organic solvent and widely used in industry, agriculture, medicine, health and daily life supplies, and other fields.
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
| Density | 920±2 | Kg/cm3 |
| Tensile Strengthat Yield | 8 | Mpa ≥ |
| Tensile Strengthat Break | 12 | Mpa ≥ |
| haze | 15 | %≤ |
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 20 | g/10min |
| Density | 0.924 | g/cm3 |
| Tensile Strength | MD12 | Mpa |
| TD 10 | ||
| Elongation at Yield | 13 | % |
| Elongation at Break | 200 | |
| Dark Drop Impact | 105 | g |
| Brittle Temperature(F 50) | -70 | C |
| Vicat Softening Point | 90 | C |
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 3.2 | g/10min |
| Density | 0.939 | g/cm3 |
| Melting Point | 127 | C |
| Tensile Yield Strength | 21 | Mpa |
| Tensile Strength at Break | 28 | Mpa |
| Elongation at Break | 1,100 | % |
| Flexural Modulus | 750 | Mpa |
| Brittle Temperature | <-60 | C |
LLDPE has penetrated almost all traditional markets for polyethylene; it is used for plastic bags and sheets (where it allows using lower thickness than comparable LDPE), plastic wrap, stretch wrap, pouches, toys, covers, lids, pipes, buckets and containers, covering of cables, geomembranes, and mainly flexible tubing.
1.Packing:
In 25kg PP woven bag, or per your requirement.
17mt/20'FCL
2.Storage:
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.